====== Double cup extrusion test ====== | ====== Double cup extrusion test ====== | ||
* Experimental friction test (Bushhausen /Altan -Ohio State University - 1992). | * Experimental friction test (Bushhausen /Altan -Ohio State University - 1992). | ||
* Mean friction coefficient is deduced from the comparison of experimental and numerical (FEM) “cup height ratios” | * Mean friction coefficient is deduced from the comparison of experimental and numerical (FEM) “cup height ratios” | ||
- | * Frictional conditions close to the forging process. | + | * Frictional conditions close to the forging process: |
* Interface pressure ~ 2500MPa. | * Interface pressure ~ 2500MPa. | ||
* Surface temperature ~600°C. | * Surface temperature ~600°C. | ||
* Surface enlargement ~3000%. | * Surface enlargement ~3000%. | ||
* Typical numerical simulation needs remeshing. | * Typical numerical simulation needs remeshing. | ||
+ | \\ | ||
+ | |||
+ | <WRAP centeralign column 100%> | ||
+ | {{url> | ||
+ | </ | ||
+ | |||
+ | {{ : | ||
+ | |||
+ | Comparison with FE results obtained using Deform2D (and remeshing). | ||
+ | |||
+ | {{ : | ||